Nondestructive flaw detection on the railway industry, the most appropriate is highly recommended to use JUT500B ultrasonic flaw detector, ultrasonic flaw detector engineer railway ultrasonic flaw detector, which is the most suitable for detection of rail flaw detection equipment, this ultrasonic flaw detector is specially designed for railway nondestructive flaw detection, is very convenient for detecting and measuring the internal defects and the discontinuity of railway track.

1. The iron works [1995] 144 document rules, the flaw detector during the season inspection, the annual inspection, the sub-branch test or the acceptance of the failure of the person must be repaired, the function goal reaches the request rear can agree to the application.
2. Iron works [1995] no. 144 document rules, when the instrument is inspected, the primary skill target fails or cannot be repaired. After the judgment of the treatment group of the road bureau, the rules can be declared and scrapped according to the rules.
3. Because the railway is affected by the wheel pressure, the railway should be flexible to offset the flexure.
4. With requirements for railway locomotive, vehicle impact dynamics, in order to cut the wheel to rail impact effect, locomotive, vehicle line cuts the crack damage of local and rail, rail must have quite a degree of steel.
5. In order to reduce the occurrence of bolt hole cracks in the railway joints, the new rail or post-processing of the railway borehole should be used to cope with the edge of the screw hole.
6. The type A shows that the ultrasonic flaw detector has the initial pulse but no reflection echo, and the pulse transmission circuit and acceptance circuit of the instrument should be focused on when determining the fault of the external cohesive unit.
7. When the incident longitudinal wave is greater than the first critical Angle and is less than the second critical Angle, and CL2 > CL1, the second medium will only exist in a transverse wave.
8. The deflection voltage of cathode ray tube is 80V, and the width of the input terminal signal is 40mV. If the signal is to reach 50% of the full width, the gain should be 60dB.
9. TB/T2340-93 specification rules: 37 ° probe detection on CTS - 60 railway block screw hole and crack on the 3 mm long, 37 ° Angle makes the wave contour, and also to reach 80% of static active degree allowance shall be not less than 22 db.
10. Iron works [1995] 144 document rules, the new head of the probe must be organized by the railway bureau, and the underlying units shall not use the special probe of the railway flaw detector without the pass of the road authority.
11. Iron works [1995] 144 document rules, after the instrument is repaired, the first skill target of the instrument must be passed the test before it can be put into use.
12. The iron works [1995] 144 document rules, after the instrument circuit is repaired, the maintenance personnel and the operator shall conduct the test together, and then fill in the inspection record form and sign it together.
13. Regulation of TB/t1632-91: the railway welding head shall be disposed of after welding.
14. Regulation of TB/t1632-91: railway welding head is broken, and micro-reflection should be made when it is difficult to judge the character of fracture defect by micro method.
15. Regulation of TB/t1632-91: no chiseled indentation, scratches and scratches are not allowed in the 100mm limit of the welding head and welding seam, and no electric breakdown shall be performed on the welding head.
16. The rules of the technical regulation, the distance between the height of the orbital plane and the distance between 1120mm ~ 3850mm, is 2000mm.
17. Ultrasonic flaw detection, for the sound beam to gather in medium 2, the lens (lens data of 1) that gathers the probe, the premise that the sound velocity of the medium 1 is greater than the speed of the medium 2.
18. Ultrasonic flaw detection, inspection near appearance defect, the most useful probe method should be the combination of the double crystal probe.
19. With ultrasonic inspection, the lower the acoustic impedance of the two kinds of data, the better the discovery of the unglued.
20. With the single oblique probe to reflect the thick weld, the defect which is perpendicular to the probe surface and large and flat is the easiest to lose.
21. In the water immersion test, the water distance between the probe and the workpiece should cause the secondary interface echo to be shown on the bottom echo.
22. TB/T2658.9-1995 rules: new construction, reconstruction and overhaul lines, and injuries, broken rail welding, shall be performed by the predecessor in the future of the ultrasonic inspection, which shall be the first certificate of inspection.
23. TB/T2658.9-1995 specification rules: on-site pressure weld and aluminum thermal weld, except for regular periodic inspection, use special instrument for welding full section inspection.
24. Rules for the maintenance of railway roadway: the total cross-section of the pressure weld at the railway site is not less than once every six months.
25. TB/T2658.9-1995 specification rules: the whole section of the railway aluminum thermal weld is not less than once every six months.
26. TB/T2658.9-1995 rules: the number of injured tracks is abnormal, and the new railway lot and over-period of the site should shorten the detection cycle.
27. TB/T2658.9-1995 specification rules: when a flaw detection device is found to be damaged (including damage). Multiple methods are used to check and verify.
28. Ultrasonic flaw detection is based on the defect echo shown on the wave screen of the instrument, which is called defect echo method.
29. The ultrasonic flaw detection is based on the height of the bottom echo, and the method of judging the defect of the specimen is called the base echo height method.
30. The pulse reflection method is not suitable for thin pieces of flaw detection.
31. The pulse reflection method ultrasonic flaw detection, because of the disturbance in the near field, the defect detection of appearance and near appearance can be worse.
32. The pulse reflection method ultrasonic flaw detection, about the acoustic beam axis of the defect, easily formed leak detection.
33. Vertical method ultrasonic flaw detection, the detection result of the best defect is the defect with the assumption plane.
34. Contact method ultrasonic flaw detection, when the thickness of the coupling layer is lambda / 4 odd times, the sound results are the worst.
35. The defects of railway welds are the most difficult to detect.
36. In order to prevent the disturbance of the longitudinal wave, the incidence Angle of the probe should be selected from above the second critical Angle.
37. To prevent the disturbance of the longitudinal wave, the Angle of incidence of the probe should be selected from the first critical Angle to the second critical Angle.
38. Gb3721-81 specification rule: a body of magnetic powder inspection machine, general magnetic power supply, clamping installation, magnetic powder spreading installation, inspection installation, demagnetization installation and other local components.
39. Gb3721-81 specification rule: a body of magnetic powder inspection machine, general magnetic power supply, clamping installation, magnetic powder spreading installation, inspection installation, demagnetization installation and other local components.
40. Gb3721-81 specification rule: a body of magnetic powder inspection machine, general magnetic power supply, clamping installation, magnetic powder spreading installation, inspection installation, demagnetization installation and other local components.
41. Gb3721-81 specification rule: a body of magnetic powder inspection machine, general magnetic power supply, clamping installation, magnetic powder spreading installation, inspection installation, demagnetization installation and other local components.
42. Gb3721-81 specification rule: a body of magnetic powder inspection machine, general magnetic power supply, clamping installation, magnetic powder spreading installation, inspection installation, demagnetization installation and other local components.
43. GB3721-81 specification rule: a body of magnetic particle inspection machine, all of the insulation resistance shall not be less than 1 m Ω.
44. The transistor consists of a common collector to expand the circuit, because the input and output loop is the public end of the collector, and the emitter is extremely output, so it is often called the emitter follower.
45. The total collector of transistor consists of a total collector, which is approximately equal to 1. The voltage expansion multiple is equal to the common emitter circuit, but the output voltage phase is the same as the input voltage phase.
46. Common emitter expanding circuit, composed of crystal triode, because the input and the output voltage phase difference of 180 °, so also called inverting amplifier.
47. Expand in transistor circuit, if the introduction of the reaction of a standard led added plus the effect of input a standard lights, and then expand circuit expand multiple get progress, so much reaction called a positive reaction.
48. In the transistor expansion circuit, if the reaction signal lamp number is introduced to weaken the effect of input signal light number, the expansion multiple decreases, then it is called negative reaction.
49. In the transistor expansion circuit, if the signal lamp is taken from the output voltage, it is called a voltage response.
50. In the transistor expansion circuit, if the signal lamp is taken from the current, it is called the current reaction.

51. It is often found that there are nuclear damage, crack degree crack, longitudinal crack and surface defect of rail head.
52. The common damage of railway mother material is nuclear injury, screw hole crack, longitudinal crack, crack of degree and surface defect of rail head.
53. The common damage of railway mother material is nuclear injury, screw hole crack, degree crack, longitudinal crack and surface defect of rail head.
54. The common injuries of railway parent materials include nuclear injury, longitudinal crack, degree crack, screw hole crack and surface defect of rail head.
55. According to the detection region, 70 ° probe is primary reflection rail head.
56. Using 70 ° probe introspection railway, advances the secondary goal is to find differences trend of reflected wave gain defects.
57. The acceptance of the necessary doping process on a semiconductor wafer makes it possible for both parties to identify the p-type semiconductor, so the layers of the two semiconductors will form a thin layer called PN junction.
58. The change of liquid in metal to a crystal is called crystallization.
59. When the metal is heated, the broken grain becomes the whole grain, and the grain of the deformation is called recrystallization.
60. The railway welding methods adopted in China are: contact welding, pressure welding and aluminum thermal welding.
61. The railway welding methods adopted in China are: contact welding, aluminum heat welding and gas pressure welding.
62. Currently, the railway welding methods adopted in China are: aluminum thermal welding, pressure welding and contact welding.
63. In railway welding, high carbon content is less weldable than low carbon content.
64. The closed loop of a magnetic induction line is called a magnetic circuit.
65. Magnetic particle detection data can only be ferromagnetic information.
66. The term "magnetic conductivity" is used to measure the difficult level of magnetization.
67. When the Angle of the incident Angle is determined, the size of the refractive Angle in the workpiece is only related to the sound velocity of the two medium
68. The task form of transistor triode is divided into three regions, and the area where the Ib is less than or equal to 0 is called the cut-off zone.
69. The task form of transistor triode is divided into three regions. When the transmitting junction is biased towards the offset, the approximate degree of the curve is called the expansion zone.
70. Triode transistor task form is divided into three regions, when the power supply Ec inevitable, Ic, Vce is small, the Ib increases again, Ic and little or no increase, triode failed to expand effect, this situation is called the saturated zone.
71. In a logic circuit, the circuit that completes the relationship with the logic is called the gate.
72. In a logic circuit, the circuit of completion or logic is called or gate.
73. In logic circuits, circuits that complete non-logical relationships are called non-gates.
74. Both input and non-gate circuits, when the input terminal A and B are all high voltage, the output should be low potential.
75. 2 input or non-gate circuit, when the input terminal A and B have A high voltage normal, the output side should be low level.
76. The defects of the railway aluminum thermal welding are slag, stomata, sand clamping, shrinkage, loose, unsoldered and crack.
77. The defects of the railway aluminum thermal welding are slag, stomata, sand clamping, shrinkage, loose, crack and unsoldered.
78. The frequent defects of the railway aluminum thermal welding are slag, porosity, sand clamping, shrinkage, unsoldered, crack and loose.
79. The defects of the railway aluminum thermal welding frequently are slag, porosity, shrinkage, loose, unsoldered, crack and sand.
80. The frequent defects of the railway aluminum thermal welding are slag, porosity, sand, loose, unsoldered, crack and shrinkage.
81. The defects commonly seen in railway aluminum thermal welding are slag, crack, sand clamping, shrinkage, loose, unsoldered, and porosity.
82. There are cracks, stomata, sand clamping, shrinkage, loose, unsoldered and slag.
83. The defects of the railway contact welding are grey, cold and overheat.
84. The defects of railway contact welding are gray, overburn and cold welding.
85. Rail contact welding frequently seen defects have been burnt, cold welding and gray patches.
86. The defects of the railway pressure welding frequently are speckle, overburn and cross section oxidation.
87. The defects of the railway pressure welding are bright spot, section oxidation and overburning.
88. The defects of railway pressure welding frequently have section oxidation, overburning and light spot.
89. Whether it is liquid metal crystallization, as well as solid metal types of phase transitions are carried out by the process of nucleation and growth.
90. When the railway flash welding, if the medium of sintering medium presents long time short circuit and speed up the fire is not less than compensation, the extremely easily formed the weld gray spot defect.
91. The residual stress of railway welding is the thermal stress due to the change of temperature.
92. When the railway contact welding, even if the end Angle does not have the oxide film, but if the interface single area does not constitute a grain, this is also an unsoldered defect.
93. The highway road maintenance rules require the railway to reflect the railway and the bifurcated railway, and the detection cycle is normally 30d.
94. When the railway flaw detector is used to reflect the railway, the railway should tell the working area and the working section in real time.
95. The cathode ray oscillograph tube is composed of electron gun, deflection system and fluorescent screen.
96. The cathode ray oscillograph tube is composed of electron gun, fluorescent screen and deflection system.
97. The cathode ray oscillograph tube is composed of fluorescent screen, deflection system and electron gun.
98. Type A shows that the scanning circuit of the railway ultrasonic flaw detector is composed of the scanning gate spreader, the sawtooth wave trigger and the sawtooth wave amplifiers.
99. Type A shows that the scanning circuit of the railway ultrasonic flaw detector is composed of the scanning gate spreader, sawtooth wave amplifiers and sawtooth paroxysms.
100. Type A shows that the scanning circuit of the railway ultrasonic flaw detector is composed of the scanning gate spreader, the sawtooth wave trigger and the sawtooth wave amplifiers.

101. Type A shows that the acceptance circuit of the special ultrasonic flaw detector in railway is composed of attenuator, high frequency amplifier, detection, control and video amplifiers.
102. Type A shows that the acceptance circuit of the special ultrasonic flaw detector in railway is composed of attenuator, high frequency amplifier, detection, control and video amplifiers.
103. Type A shows that the acceptance circuit of the special ultrasonic flaw detector in railway is composed of attenuator, high frequency amplifier, control, detection and video amplifiers.
104. Type A shows that the acceptance circuit of the special ultrasonic flaw detector in railway is composed of attenuator, high frequency amplifier, detection, control and video amplifiers.
105. Type A shows that the acceptance circuit of the special ultrasonic flaw detector in railway is composed of attenuator, high frequency amplifier, detection, control and video amplifiers.
106. Type A shows that when the transmission circuit of the special ultrasonic flaw detector of the railway is divided, the resolution of the instrument will be affected.
107. When using an oscilloscope to view the voltage amplitude of the measured circuit, the knob and range switch on the Y axis should be selected properly.
108. When using an oscilloscope to view the frequency of the measured circuit, select the knob and range switch relating to the X-axis.
109. Type A display ultrasonic flaw detector, in order to make the scanning process display on the fluorescent screen and the circuit which does not display on the reverse course is called the enhancement circuit.
110. The type A shows ultrasonic flaw detector, which shows the reflection echo from the bottom up to the fluorescent screen, and the flag signal should be turned on the plate.
111. Ultrasonic flaw detection, to obtain the invariable coupling form, on the surface of the probe can be added with arc contact block.
112. The contact method is used to detect the sound pressure in the acoustic beam in the near field. Therefore, it is not common to carry out quantitative detection in the near field.
113. When using the contact method to detect the workpiece at close intervals (or small diameter), a smaller diameter wafer can be used to obtain the high acoustic limit.
114. When the detection interval is large, the chip with larger diameter should be used to obtain more concentrated energy.
115. Contact method superprobe, with the base wave height method to adjust the activity of the activity of the coupling poor, the thickness of the deep part of the defect can also be compensated for the material attenuation.
116. The defect of the diameter of the beam is greater than the diameter of the beam, and the defect can be measured by 6dB method or half wave height method.
117. GB9445-88 specification rule: the skills of nondestructive testing personnel qualifications are divided into three grades, levels Ⅲ for first-class, Ⅱ for intermediate level, Ⅰ as the primary.
118. GB9445-88 specification rules: Ⅰ nondestructive testing personnel should possess at levels Ⅱ or Ⅲ monitoring staff, under the guidance, according to skill package insert for nondestructive testing.
119. GB9445-88 specification rules: Ⅰ nondestructive testing personnel should possess at levels Ⅱ or Ⅲ monitoring staff, under the guidance, can adjust and use of instruments and equipment.
120. GB9445-88 specification rules: Ⅰ nondestructive testing personnel should possess at levels Ⅱ or Ⅲ monitoring staff, under the guidance, testing operation.
121. GB9445-88 specification rules: Ⅰ nondestructive testing personnel should possess at levels Ⅱ or Ⅲ monitoring staff, under the guidance, according to the specification for initial grading test consequences.
122. GB9445-88 specification rules: Ⅱ nondestructive testing personnel should be based on the determination of process, prepare the package insert.
123. GB9445-88 specification rules: Ⅱ nondestructive testing personnel should be able to device and calibrated instruments and equipment.
124. GB9445-88 specification rules: Ⅱ nondestructive testing personnel should be able to detailed implementation of nondestructive testing.
125. GB9445-88 specification rules: Ⅱ nondestructive testing personnel should be able to according to the rules, norms and standards, analysis and evaluation of test results.
126. GB9445-88 specification rules: Ⅱ nondestructive testing personnel should be able to write a declaration, issued by detecting the consequences.
127. GB9445-88 specification rules: Ⅱ level of nondestructive testing personnel should be familiar with nondestructive testing method using limited limitations.
128. GB9445-88 specification rules: Ⅱ nondestructive testing personnel should be able to training and guidance Ⅰ level staff cadets monks did not obtain evidence.
129. GB9445-88 specification rules: Ⅲ nondestructive testing personnel coping skills and determine nondestructive testing technology, implementing rules, norms, standards and other bear all responsibility.
130. GB9445-88 specification rules: Ⅲ nondestructive testing personnel should be concrete nondestructive testing task of monitoring, governance.
131. GB9445-88 specification rules: Ⅲ nondestructive testing personnel should be according to the rules, norms and standards, analysis and evaluation of test results.
132. GB9445-88 specification rules: Ⅲ nondestructive testing personnel should be able to design a special nondestructive testing methods, skills and process.
133. GB9445-88 specification rules: Ⅲ level nondestructive testing personnel should be no acceptance specification is available for use, assist relevant part in acceptance specification.
134. GB9445-88 specification rules: Ⅲ nondestructive testing personnel should have data, structure and production process in the practice of common sense and common to familiar with other NDT methods.
135. GB9445-88 specification rules: levels Ⅲ nondestructive testing personnel should be able to train Ⅰ and Ⅱ level personnel.
136. GB9445-88 specification rules: Ⅲ nondestructive testing personnel is engaged in each kind of nondestructive test method test content includes: life common sense, to common sense and theory to three aspects.
137. GB9445-88 specification rules: Ⅲ nondestructive testing personnel is engaged in each kind of nondestructive test method test content includes: life common sense, to common sense and theory to three aspects.
138. GB9445-88 specification rules: Ⅲ nondestructive testing personnel is engaged in each kind of nondestructive test method test content includes: life common sense way can sense and theory from three aspects.
139. Rule of gb9445-88: every test result for non-destructive testing personnel should be scored on a percentage basis, and the results of written examinations and operational tests should be at least 70 points.
140. The binary four operations are also performed like the decimal four operations, with only the requirements of "two in one, one for two".
141. A decimal number can be used to reveal the performance of four binary Numbers. The commonly used exchange code is 8421 - BCD code.
142. The common computer is called the host of the calculating machine, the regulator and the memory.
143. The operator of an accounting machine is called the center disposer.
144. The memory in the accounting machine belongs to the main memory, the hard disk belongs to the auxiliary memory.
145. The memory in the accounting machine belongs to the main memory, the hard disk belongs to the auxiliary memory.
146. In the magnetic particle inspection, the induction current method is used to detect the defect of the circular deviation of the circular workpiece by using the magnetization method.
147. In the magnetic particle inspection, the rod magnetization method should be used to make the outer surface of the hollow workpiece surface and the end surface of the magnetic field.
148. In order to detect the small defects in the appearance of the workpiece, it is better to choose the small magnetic powder.
149. The magnetic powder detection is easy to see, which should be applied to the surface of the workpiece with a magnetic powder that is more than the color of the light.
150. Magnetic particle detection, the method of applying magnetic particle inspection after the loss of magnetic field is called residual magnetic method.